Bandstahl Werkstoffe
Martensitische rostbeständige Edelstähle
Werkstoffe |
Chemische Zusammensetzung |
Mechanische Eigenschaften |
|||||||||||||||||
EN- |
EN- |
ASTM/ |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Sonstige |
Rp0,2 [N/mm²] |
Rm [N/mm²] |
A80 [min.%] |
PRE |
||||
1.4021 |
X20 Cr13 |
420 |
0,16 - |
≤ 1,00 |
≤ 1,50 |
≤ 0.040 |
≤ 0.015 |
12,0-14,0 |
–- |
– |
– |
– |
≤ 700 |
15 |
13 |
||||
1.4028 |
X30 Cr13 |
420 |
0,26 - |
≤ 1,00 |
≤ 1,50 |
≤ 0.040 |
≤ 0.015 |
12,0-14,0 |
– |
– |
– |
– |
≤ 740 |
15 |
14 |
||||
1.4034 |
X46 Cr13 |
420 |
0,43 – |
≤ 1,00 |
≤ 1,00 |
≤ 0.040 |
≤ 0.015 |
12,5-14,5 |
– |
– |
– |
– |
≤ 780 |
12 |
14 |
||||
1.4037 |
X65 Cr13 |
420 |
0,58 – |
≤ 1,00 |
≤ 1,00 |
≤ 0.045 |
≤ 0.015 |
12,5-14,5 |
– |
– |
– |
– |
≤ 840 |
12 |
|||||
1.4057 |
X17CrNi16-2 |
431 |
0,12 – |
≤ 1,00 |
≤ 1,50 |
≤ 0.040 |
≤ 0.015 |
15,0-17,0 |
1,5 – 2,5 |
– |
– |
– |
≤ 840 |
12 |
16 |
||||
1.4104 |
X14CrMoS17 |
430F |
0,10 – |
≤ 1,00 |
≤ 1,50 |
≤ 0.040 |
0.015 – 0,035 |
15,5-17,5 |
– |
0,20 – 0,60 |
– |
– |
≤ 840 |
12 |
17 |
||||
1.4112 |
X90CrMOV18 |
440B |
0,85 – |
≤ 1,00 |
≤ 1,00 |
≤ 0.040 |
≤ 0.015 |
17,0-19,0 |
– |
0,90 – 1,30 |
V 0,07 – 0,12 |
– |
≤ 840 |
12 |
22 |
||||
1.4122 |
X39CrMo17-1 |
– |
0,33 – |
≤ 1,00 |
≤ 1,50 |
≤ 0.040 |
≤ 0.015 |
15,5-17,5 |
≤ 1,00 |
0,80 – 1,30 |
– |
– |
≤ 900 |
12 |
20 |
Andere Werkstoffe auf Anfrage. Alle Angaben sind ohne Gewähr.
Austenitische rostbeständige Edelstähle
Werkstoffe |
Chemische Zusammensetzung |
Mechanische Eigenschaften |
|||||||||||||||||
EN- |
EN- |
ASTM/ |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Sonstige |
Rp0,2 [N/mm²] |
Rm [N/mm²] |
A80 [min.%] |
PRE |
||||
1.4301/ |
X5 CrNi 18-10 |
304 / 304 S |
≤ 0,07 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
17,0-19,5 |
8,0-10,5 |
– |
N ≤ 0,11 |
≥ 230 |
540-750 |
45 |
19 |
||||
1.4303/ |
X4 CrNi 18-12 |
305 / 305 S |
≤ 0,06 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
17,0-19,0 |
11,0-13,0 |
– |
N ≤ 0,11 |
≥ 220 |
500-650 |
45 |
20 |
||||
1.4305 |
X8 CrMoS18-9 |
303S |
≤ 0,10 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
0.015 – 0,350 |
17,0-19,0 |
8,0-11,0 |
– |
N ≤ 0,11 Cu ≤ 1.0 |
≥ 220 |
520-670 |
45 |
20 |
||||
1.4306 |
X2 CrNi 19-11 |
304 L |
≤ 0,03 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
18,0-20,0 |
10,0-12,0 |
– |
N ≤ 0,11 |
≥ 220 |
520-670 |
45 |
21 |
||||
1.4307 |
X2CrNi18-9 |
~304 L |
≤ 0,03 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
17,5-19,5 |
8,0-10,0 |
– |
N ≤ 0,11 |
≥ 220 |
520-670 |
45 |
20 |
||||
1.4310 |
X10 CrNi 18-8 |
301 |
0,05-0,15 |
≤ 2,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
16,0-19,0 |
6,0-9,5 |
≤ 0,80 |
N ≤ 0,11 |
≥ 250 |
900-2200 |
40³ |
|||||
1.4318 |
X2 CrNiN 18-7 |
301 LN |
≤ 0,03 |
– |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
16,5-18,5 |
6,5-8,0 |
– |
N ≤ 0,20 |
≥ 350 |
650-850 |
≥ 35 |
|||||
1.4372 |
X12 CrMnNiN 17-7-5 |
201 |
≤ 0,15 |
≤ 1,00 |
5,50-7,50 |
≤ 0.045 |
≤ 0.015 |
16,0-18,0 |
3,50-5,50 |
– |
N 0,05-0,25 |
350 |
850-1700 |
45³ |
|||||
1.4401 |
X5 CrNiMo 17-12-2 |
316 |
≤ 0,07 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
16,5-18,5 |
10,0-13,0 |
2,0 - 2,5 |
N ≤ 0,11 |
≥ 220 |
530-680 |
40 |
27 |
||||
1.4404 |
X2 CrNiMoN 17-12-2 |
316 L |
≤ 0,03 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
16,5-18,5 |
10,0-13,0 |
2,0 - 2,5 |
N ≤ 0,11 |
≥ 240 |
530-680 |
40 |
27 |
||||
1.4429 |
X2CrNiMoN17-13-3 |
316LN |
≤ 0,03 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.025 |
16,5-18,5 |
11,0-14,0 |
2,5 – 3,0 |
N 0,12 – 0,25 |
29 |
|||||||
1.4432 |
X2CrNiMo17-12-3 |
– |
≤ 0,03 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
16,5-18,5 |
10,5-13,0 |
2,5 – 3,0 |
N ≤ 0,11 |
28 |
|||||||
1.4435 |
X2CrNiMo18-14-3 |
316L |
≤ 0,03 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
17,0-19,0 |
12,5-15,0 |
2,5 – 3,0 |
N ≤ 0,11 |
29 |
|||||||
1.4436 |
X3CrNiMo17-13-3 |
316 |
≤ 0,05 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
16,5-18,5 |
10,5-13,0 |
2,5 – 3,0 |
N ≤ 0,11 |
28 |
|||||||
1.4438 |
X2CrNiMo18-15-4 |
317L |
≤ 0,03 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
17,5-19,5 |
13,0-16,0 |
3,0 – 4,0 |
N ≤ 0,11 |
32 |
|||||||
1.4441 |
X2CrNiMo18-15-3 |
316LVM |
≤ 0,03 |
≤ 1,00 |
≤ 2,00 |
≤ 0.025 |
≤ 0.010 |
17,5-18,5 |
13,5-15,5 |
2,7 – 3,2 |
N ≤ 0,10 |
29 |
|||||||
1.4541 |
X6CrNiTi18-10 |
321 |
≤ 0,08 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
17,0-19,0 |
9,0-12,0 |
– |
Ti =(5x % C) (≤ 0,70) |
≥ 240 |
520-720 |
40 |
18 |
||||
1.4571 |
X6CrNiTi17-12-2 |
316Ti |
≤ 0,08 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
16,5-18,5 |
10,5-13,5 |
2,0 – 2,5 |
≤ 0,070 |
≥ 270 |
540-690 |
40 |
25 |
||||
1.4597 |
X8CrMnCuNB17-8-3 |
204Cu |
≤ 0,07 |
0,50 – 1,50 |
6,50 – 8,50 |
≤ 0.040 |
≤ 0.010 |
16,0-17,0 |
1,50 – 2,00 |
0,20 – 0,50 |
Cu 2,50 – 3,50 N 0,15 – 0,30 |
Andere Werkstoffe auf Anfrage. Alle Angaben sind ohne Gewähr.
Super Austenitische rostbeständige Edelstähle
Werkstoffe |
Chemische Zusammensetzung |
Mechanische Eigenschaften |
|||||||||||||||||
EN- |
EN- |
ASTM/ |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Sonstige |
Rp0,2 [N/mm²] |
Rm [N/mm²] |
A80 [min.%] |
PRE |
||||
1.4529 |
X1NiCrMoCuN25-20-7 |
– |
≤ 0,02 |
≤ 0,50 |
≤ 1,00 |
≤ 0.030 |
≤ 0.010 |
19,0- 21,0 |
24,0 – |
6,0 – |
Cu 0,50 – 1,50 |
≥ 320 |
420-640 |
20 |
45 |
||||
1.4539 |
X1NiCrMoCuN25-20-5 |
904L |
≤ 0,02 |
≤ 0,70 |
≤ 2,00 |
≤ 0.030 |
≤ 0.010 |
19,0- 21,0 |
24,0 – |
4,0 – |
Cu 1,20 – 2,00 |
≥ 240 |
530-730 |
35 |
37 |
Andere Werkstoffe auf Anfrage. Alle Angaben sind ohne Gewähr.
Hitze – und Kriechbeständige Edelstähle
Werkstoffe |
Chemische Zusammensetzung |
Mechanische Eigenschaften |
|||||||||||||||||
EN- |
EN- |
ASTM/ |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Sonstige |
Rp0,2 [N/mm²] |
Rm [N/mm²] |
A80 [min.%] |
PRE |
||||
1.4828 |
X15CrNiSi20-12 |
309 |
≤ 0,20 |
1,50 – 2,50 |
≤ 2,00 |
≤ 0.045 |
≤ 0.030 |
19,0- 21,0 |
11,0 – 13,00 |
– |
N ≤ 0,11 |
≥ 230 |
500-700 |
30 |
22 |
||||
1.4833 |
X12CrNi23-13 |
309S |
≤ 0,15 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.015 |
22,0- 24,0 |
12,0 – 14,00 |
– |
N ≤ 0,11 |
≥ 230 |
500-700 |
30 |
25 |
||||
1.4878 |
X8CrNiTi18-10 |
321H |
≤ 0,12 |
≤ 1,00 |
≤ 2,00 |
≤ 0.045 |
≤ 0.030 |
17,0- 19,0 |
9,0 – 12,00 |
– |
Ti =(4 x % C) (≤ 0,80) |
≥ 230 |
500-700 |
30 |
18 |
Andere Werkstoffe auf Anfrage. Alle Angaben sind ohne Gewähr.
Duplex Edelstähle
Werkstoffe |
Chemische Zusammensetzung |
Mechanische Eigenschaften |
|||||||||||||||||
EN- |
EN- |
ASTM/ |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Sonstige |
Rp0,2 [N/mm²] |
Rm [N/mm²] |
A80 [min.%] |
PRE |
||||
1.4062 |
X2CrNiN22-2 |
– |
≤ 0,020 |
≤ 1,00 |
≤ 2,00 |
≤ 0.040 |
≤ 0.030 |
21,0 -22.0 |
1,50 -2.0 |
≤ 0.45 |
Cu ≤ 0,50 N ≤ 0,20 |
≥ 450 |
≥ 650 |
30 |
|||||
1.4162 |
X2CrMnNiN22-5-2 |
– |
≤ 0,030 |
≤ 1,00 |
≤ 5,00 |
≤ 0.040 |
≤ 0.030 |
21,0 – 22,0 |
1.35-1.70 |
≤ 0.50 |
Cu ≤ 0,50 N ≤ 0,25 |
≥ 450 |
≥ 665 |
30 |
26 |
||||
1.4362 |
X2CrNiN23-4 |
– |
≤ 0,030 |
≤ 1,00 |
≤ 2,00 |
≤ 0.035 |
≤ 0.015 |
22,0- 24,0 |
3.5 – 5.5 |
≤ 0.60 |
Cu ≤ 0,60 N ≤ 0,20 |
≥ 400 |
≥ 630 |
25 |
27 |
||||
1.4462 |
X2CrNiMoN22-5-3 |
– |
≤ 0,030 |
≤ 1,00 |
≤ 2,00 |
≤ 0.030 |
≤ 0.015 |
21,0- 23.0 |
4.5 – 6.5 |
2.5 – 3.5 |
N ≤ 0,22 |
≥ 460 |
≥ 640 |
25 |
34 |
Andere Werkstoffe auf Anfrage. Alle Angaben sind ohne Gewähr. Sonderstähle auf Anfrage.
Unlegierte Edelstähle Gütenorm 10132-4
Werkstoffe |
Chemische Zusammensetzung |
Mechanische Eigenschaften |
|||||||||||||||||
EN- |
EN- |
ASTM/ |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Sonstige |
Rp0,2 [N/mm²] |
Rm [N/mm²] |
A80 [min.%] |
PRE |
||||
1.1204 |
C55S |
0.52-0.60 |
0.15-0.35 |
0.60-0.90 |
≤ 0.025 |
≤ 0.025 |
≤ 0.40 |
≤ 0.40 |
≤ 0.10 |
||||||||||
1.1211 |
C60S |
1060 |
0,57-0,65 |
0,15-0,35 |
0,60-0,90 |
≤ 0.025 |
≤ 0.025 |
≤ 0.40 |
≤ 0.40 |
≤ 0.10 |
495 |
620 |
17 |
||||||
1.1217 |
C90S |
0.85-0.95 |
0.15-0.35 |
0.40-0.70 |
≤ 0.025 |
≤ 0.025 |
≤ 0.40 |
≤ 0.40 |
≤ 0.10 |
||||||||||
1.1224 |
C125S |
1.20-1.30 |
0.15-0.35 |
0.30-0.60 |
≤ 0.025 |
≤ 0.025 |
≤ 0.40 |
≤ 0.40 |
≤ 0.10 |
||||||||||
1.1231 |
C67S |
1070 |
0,65-0,73 |
0,15-0,35 |
0,60-0,90 |
≤ 0.025 |
≤ 0.025 |
≤ 0.40 |
≤ 0.40 |
≤ 0.10 |
510 |
640 |
16 |
||||||
1.1248 |
C75S |
1074/ 1075/ 1078 |
0,70-0,80 |
0,15-0,35 |
0,60-0,90 |
≤ 0.025 |
≤ 0.025 |
≤ 0.40 |
≤ 0.40 |
≤ 0.10 |
510 |
640 |
15 |
||||||
1.1269 |
C85S |
1086 |
0,80-0,90 |
0,15-0,35 |
0,40-0,70 |
≤ 0.025 |
≤ 0.025 |
≤ 0.40 |
≤ 0.40 |
≤ 0.10 |
535 |
670 |
15 |
||||||
1.1274 |
C100S |
1095 |
0,95-1,05 |
0,15-0,35 |
0,30-0,60 |
≤ 0.025 |
≤ 0.025 |
≤ 0.40 |
≤ 0.40 |
≤ 0.10 |
550 |
690 |
13 |
||||||
1.5021 |
48Si7 |
0.45-0.52 |
1.60-2.00 |
0.50-0.80 |
≤ 0.025 |
≤ 0.025 |
≤ 0.40 |
≤ 0.40 |
≤ 0.10 |
||||||||||
1.5026 |
56Si7 |
0.52-0.60 |
1.60-2.00 |
0.60-0.90 |
≤ 0.025 |
≤ 0.025 |
≤ 0.40 |
≤ 0.40 |
≤ 0.10 |
||||||||||
1.2002 |
125Cr1 |
- |
1,20-1,30 |
0,15-0,35 |
0,25-0,40 |
≤ 0.025 |
≤ 0.025 |
0,4-0,6 |
≤ 0.40 |
≤ 0.10 |
590 |
750 |
11 |
||||||
1.2018 |
95Cr1 |
0.90-1.00 |
0.15 - 0.30 |
0.20-0.40 |
≤ 0.025 |
≤ 0.025 |
0.30-0.40 |
≤ 0.40 |
≤ 0.10 |
||||||||||
1.2067 |
102Cr6 |
0.95-1.10 |
0.15-0.35 |
0.20-0.40 |
≤ 0.025 |
≤ 0.025 |
1.35-1.60 |
≤ 0.40 |
≤ 0.10 |
||||||||||
1.3505 |
100Cr6 |
0,95-1,05 |
0,15-0,35 |
0,90-1,50 |
≤ 0.025 |
≤ 0.025 |
1.30-1.50 |
≤ 0.40 |
≤ 0.10 |
||||||||||
1.7701 |
51CrMoV4 |
– |
0,48 – 0,56 |
0,15 – 0,40 |
0,70 – 1,10 |
≤ 0.030 |
≤ 0.030 |
0,90-1.25 |
– |
0,15 – 0,25 |
V 0,08 – 0,12 |
||||||||
1.8159 |
51CrV4 |
6145 |
0,47-0,55 |
≤ 0,40 |
0,70-1,10 |
≤ 0.025 |
≤ 0.025 |
0,9-1,2 |
≤ 0.40 |
≤ 0.10 |
V 0,10-0,25 |
550 |
700 |
13 |
|||||
51CrMo3-2 |
0.52 |
0.90 |
0.68 |
≤ 0.025 |
≤ 0.025 |
2.96 |
0.24 |
1.49 |
V 0.38 |
||||||||||
1.5634 |
75Ni8 |
0.72-0.78 |
0.15-0.35 |
0.30-0.50 |
≤ 0.025 |
≤ 0.025 |
< 0.15 |
1.80-2.10 |
< 0.10 |
Material auch lieferbar in gehärteter und angelassener Ausführung (Rm ca. 1000 - 2000 N/mm²). Weitere Werkstoffe und Varianten im Programm (individuelle Anfragen). Alle Angaben sind ohne Gewähr.
Werkzeugstähle
Werkstoffe |
Chemische Zusammensetzung |
Mechanische Eigenschaften |
|||||||||||||||||
EN- |
EN- |
ASTM/ |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Sonstige |
Rp0,2 [N/mm²] |
Rm [N/mm²] |
A80 [min.%] |
PRE |
||||
1.2235 |
80CrV2 |
0.75-0.85 |
0.25-0.40 |
0.30-0.50 |
≤ 0.030 |
≤ 0.030 |
0.40-0.70 |
≤ 0.40 |
< 0.10 |
V 0.15-0.25 |
|||||||||
1.2345 |
X50CrMoV5-1 |
A8 |
0,50 |
1,10 |
0,40 |
≤ 0,030 |
≤ 0,030 |
5,30 |
– |
1,30 |
V 0,40 |
||||||||
1.2360 |
X50CrMoV8-1 |
A8 |
0,50 |
0,90 |
0,50 |
≤ 0,030 |
≤ 0,030 |
8,50 |
– |
1,20 |
V 0,50 |
||||||||
~ 1.2357 |
50CrMoV13-14 |
S7 |
0,50 |
0,25 |
0,50 |
≤ 0,030 |
≤ 0,030 |
3,25 |
– |
1,45 |
V 0,20 |
||||||||
1.2363 |
X100CrMoV5 |
A2 |
1,00 |
0,35 |
0,40 |
≤ 0,030 |
≤ 0,030 |
5,0 |
– |
0,95 |
V 0,20 |
||||||||
1.2365 |
X32CrMoV3-3 |
0,28-0,35 |
0,10-0,40 |
0,15-0,45 |
≤ 0,030 |
≤ 0,030 |
2,70-3,20 |
– |
2,60 – 3,00 |
V 0,40-0,70 |
|||||||||
1.2379 |
X153CrMoV12 |
D2 |
1,53 |
0,25 |
0,45 |
≤ 0,035 |
≤ 0,035 |
12,0 |
– |
0,85 |
V 0,86 |
||||||||
1.2436 |
X210CrW12 |
D6 |
2,15 |
0,25 |
0,45 |
≤ 0,035 |
≤ 0,035 |
12,0 |
– |
– |
W 0,70 |
||||||||
1.2567 |
X30WCrV5-3 |
– |
0,30 |
0,25 |
0,30 |
≤ 0,035 |
≤ 0,035 |
2,35 |
– |
– |
V 0,60 W 4,25 |
Material auch lieferbar in gehärteter und angelassener Ausführung (Rm ca. 1000 - 2000 N/mm²). Weitere Werkstoffe und Varianten im Programm (individuelle Anfragen). Alle Angaben sind ohne Gewähr.